- B2B Metal and Engineering Marketplace
- Alloy Steel
- Aluminium
- Carbon Steel
- Copper Alloy
- Hardox Plate
- Metal Cutting Services
- Nickel Alloy
- Plastic Mould Steel
- Precision Ground Plate
- Stainless Steel
- Stainless Steel Shim Plate , Carbon Steel Shim Plate
- Structure Steel
- Titanium
- Tool Steel
- Others
E STEEL SDN. BHD.
No 1 & 3, Lorong Sungai Puloh 7/KU6, Kawasan Perindustrian Sungai Puloh, 42100 Klang, Selangor, Malaysia.
+603-3292 8686
Titanium Grade 5 | TI6AL4V Titanium | Titanium Alloy
| Previous | 6 / 7 | Next |
- Titanium Grade 5 Ti6Al4V Suppliers Singapore
- Titanium Grade 5 Ti6Al4V Suppliers Indonesia
- Titanium Round Bars Rods Shafts Suppliers
- Titanium Plates Sheets Suppliers
We are the Leading Supplier of Titanium Grade 5 (Ti6Al4V).
We export to Singapore , Indonesia , Brunei and other ASEAN Countries.
Our specialty is to provide wide range of stainless steel with no minimum order.
E Steel supply Titanium Grade 5 (Ti6Al4V) Round Bars / Rods / Shafts , Titanium Grade 5 (Ti6Al4V) Plates. (Japan , UK Origin)
Description
Grade 5 alloy is easily welded in the annealed condition, or in the solution and partially aged condition, with aging being completed during the post weld heat treatment. Precautions must be taken to prevent oxygen, nitrogen, and hydrogen contamination. Fusion welding can be done in inert gas filled chambers, or using inert gas welding of the molten metal and the adjacent heated zones using a trailing shield.
Spot, seam, and flash welding can be performed without resorting to protective atmospheres.
MACHINABILITY The alloy can be machined using practices for austenitic steels with slow speeds, heavy feeds, rigid tooling and large amounts of non-chlorinated cutting fluid
Heat Treatment
Solution treat at 904-954 C(1660-1750 F) for 2 hours followed by water quench.
Forging
Rough forge at 982 C(1800 F), finish at @ 968 C (1750 C).
Hot Working
Hot forming will reduce both the springback and required forming forces, and will increase the overall ductility of the material.
Cold Working
The cold working characteristics of this material are similar to those of austenitic stainless steels. In multiple forming operations, intermediate stress relieving is recommended to offset the alloy’s tendency to work harden. Post-work annealing is required to re-attain optimum performance characteristics.
Annealing
Hold at 732 C(1350 F) between 1/4 and 4 hours, Furnace cool to 566 C(1050 F) then air cool. Furnace cooling is not required for forgings and bars.
Aging
Age at 538 C (1000 F) for 4 hours, air cool.
We export to Singapore , Indonesia , Brunei and other ASEAN Countries.
Our specialty is to provide wide range of stainless steel with no minimum order.
E Steel supply Titanium Grade 5 (Ti6Al4V) Round Bars / Rods / Shafts , Titanium Grade 5 (Ti6Al4V) Plates. (Japan , UK Origin)
Description
Titanium Grade 5 Suppliers - Ti6AL4V , Titanium Alloy Ti 6-4 , AMS Spec
Grade 5 Titanium Alloy , also known as Ti6Al4V, Ti-6Al-4V or Ti 6-4, is the most commonly used alloy. It has a chemical composition of 6% aluminium, 4% vanadium, 0.25% (maximum) iron, 0.2% (maximum) oxygen, and the remainder titanium.[5] It is significantly stronger than commercially pure titanium while having the same stiffness and thermal properties (excluding thermal conductivity, which is about 60% lower in Grade 5 Ti than in CP Ti).[6] Among its many advantages, it is heat treatable. This grade is an excellent combination of strength, corrosion resistance, weld and fabricability.Chemical Composition of Titanium Grade 5
| Weight % | Al | V | Fe | N | C | O | H | Ti |
| Min. | 5,5 | 3,5 | ||||||
| Max. | 6,8 | 4,5 | 0,25 | 0,05 | 0,08 | 0,2 | 0,015 | BAL. |
Related Specifications of Ti6Al4V (Grade 5)
- UNS R56400
- ASTM B348 (Grade 5)
- 3.7164
- 3.7165
Mechanical Properties of Ti6AL4V , Titanium Grade 5
| Property | Minimum | Typical Value |
| Tensile Strength MPa (ksi) | 897 (130) | 1000 (145) |
| 0.2% Proof Stress MPa (ksi) | 828 (120) | 910 (132) |
| Elongation Over 2 Inches % | 10 | 18 |
| Reduction in Area % | 20 | |
| Elastic Modulus GPa (Msi) | 114 (17) | |
| Hardness Rockwell C | 36 | |
| Specified Bend Radius <0.070 in x Thickness | 4.5 | |
| Specified Bend Radius >0.070 in x Thickness | 5.0 | |
| Welded Bend Radius x Thickness | 6 | |
| Charpy, V-Notch Impact J (ft.lbf) | 24 (18) |
Weldability
Grade 5 alloy is easily welded in the annealed condition, or in the solution and partially aged condition, with aging being completed during the post weld heat treatment. Precautions must be taken to prevent oxygen, nitrogen, and hydrogen contamination. Fusion welding can be done in inert gas filled chambers, or using inert gas welding of the molten metal and the adjacent heated zones using a trailing shield.
Spot, seam, and flash welding can be performed without resorting to protective atmospheres.
MACHINABILITY The alloy can be machined using practices for austenitic steels with slow speeds, heavy feeds, rigid tooling and large amounts of non-chlorinated cutting fluid
Heat Treatment
Solution treat at 904-954 C(1660-1750 F) for 2 hours followed by water quench.
Forging
Rough forge at 982 C(1800 F), finish at @ 968 C (1750 C).
Hot Working
Hot forming will reduce both the springback and required forming forces, and will increase the overall ductility of the material.
Cold Working
The cold working characteristics of this material are similar to those of austenitic stainless steels. In multiple forming operations, intermediate stress relieving is recommended to offset the alloy’s tendency to work harden. Post-work annealing is required to re-attain optimum performance characteristics.
Annealing
Hold at 732 C(1350 F) between 1/4 and 4 hours, Furnace cool to 566 C(1050 F) then air cool. Furnace cooling is not required for forgings and bars.
Aging
Age at 538 C (1000 F) for 4 hours, air cool.
Applications of Grade 5 Titanium
Titanium Grade 5 is a pure alpha-beta titanium with aluminum as the alpha stabilizer and vanadium as the beta stabilizer. This alloy is primarily use for corrosion resistance and is the most widely used specification in all product forms. The alloy features very high strength, good corrosion resistance, excellent strength to weight ratio and high strength at cryogenic temperatures.
Our Sales & Supplier Network
Australia, Pakistan, Malaysia, Singapore, Taiwan, China,Vietnam, Belgium, Japan, South Korea, Philippines, France, United Kingdom, Indonesia, Thailand, Hong Kong, China, Sweden, United States, Dubai, Finland, Brunei,Germany.
E Steel is a Global Metal Procurement Company in providing and sourcing raw materials to the wide range of engineering industries / sectors. We works as the the Online B2B Metal Marketplace to help our customers in finding the special steels that might feel hard to source locally.